Pineapple (BL) in the opening CERAMIC BALLS CERAMIC BALLS inertia on the basis of the development of new products to a sphere diameter hole axis, as well as with certain mechanical strength and chemical stability. Acid, alkali - resistant, heat resistant than tables, high porosity, reduced resistance to a more uniform distribution of gas-liquid flow increased, and not compacted catalyst, not charred, extended catalyst life.
Specifications
|
Performance
|
Indicators
|
|
Water absorption (％)
|
≤5
|
|
Packing density (kg/m3)
|
1200—1550
|
|
Proportion (g/cm3)
|
2.3—2.45
|
|
Scorching weightlessness (w/w．％)
|
0.25-0.45
|
|
Resistance temperature (℃)
|
1300-1600
|
|
Mo's hardness (level)
|
≥7
|
|
the acid resistance (％)
|
≥98
|
|
the acid resistance (％)
|
≥82
|
|
Blastic resistance temperature (℃)
|
800-20 not cracked three
|
|
Softening degrees (℃)
|
1970
|
Specifications
|
BL Opening CERAMIC BALLS
|
Inert CERAMIC BALLS
|
|
Specifications (mm)
|
Aperture
(mm)
|
Specific Surface Area
(m2m3)
|
voidage (％)
|
Compressive strength
(KN/ grain)
|
Specifications (mm)
|
Aperture
(m2m3)
|
Specific Surface Area
(％)
|
Compressive strength
(KN/ grain)
|
|
Φ13
|
2
|
381.5
|
34.1
|
≥1.10
|
Φ13
|
301.6
|
30.1
|
≥1.10
|
|
Φ16
|
2
|
349.6
|
34.O
|
≥1.60
|
Φ16
|
260.5
|
30.6
|
≥1.60
|
|
Φ20
|
3
|
260.8
|
33.1
|
≥2.OO
|
Φ20
|
210.8
|
28.4
|
≥2.OO
|
|
Φ25
|
4
|
207.9
|
32.5
|
≥2.80
|
Φ25
|
158.2
|
29.2
|
≥2.80
|
|
Φ30
|
5
|
172.8
|
32.2
|
≥3.20
|
Φ30
|
138.2
|
29.1
|
≥3.20
|
|
Φ50
|
7
|
104.O
|
32.5
|
≥6.50
|
Φ50
|
80.2
|
29.O
|
≥6.50
|
Chemical Composition
|
Al203+Si02
|
T102
|
Fe203
|
Ca0
|
Mg0
|
K20
|
Na20
|
|
>90％
|
<O.5％
|
<1％
|
<1.2％
|
<1％
|
<2.4％
|
<1.2％
|
|
|
|
|
|
|
|
|
|